Abstract
We demonstrate monolithic aluminum gallium arsenide (AlGaAs) optical nanoantennas. Using a selective oxidation technique, we fabricated epitaxial semiconductor nanocylinders on an aluminum oxide substrate. Second harmonic generation from AlGaAs nanocylinders of 400 nm height and varying radius pumped with femtosecond pulses delivered at 1554-nm wavelength has been measured, revealing a peak conversion efficiency exceeding 10−5 for nanocylinders with an optimized geometry.
Domains
Optics [physics.optics]
Fichier principal
oe-24-14-15965.pdf (2.54 Mo)
Télécharger le fichier
oe-29-7-11132.pdf (2.15 Mo)
Télécharger le fichier
Origin : Publisher files allowed on an open archive
Format : Figure, Image
Licence : CC BY - Attribution
Comment : Erratum (2021) : Figure 1(b) in [V. F. Gili et al, Opt. Express 24, 15965 (2016) is corrupted and is corrected in this erratum. https://doi.org/10.1364/OE.425110
Licence : CC BY - Attribution
Comment : Erratum (2021) : Figure 1(b) in [V. F. Gili et al, Opt. Express 24, 15965 (2016) is corrupted and is corrected in this erratum. https://doi.org/10.1364/OE.425110